A Study of the Long-Term Electrochemical Stability of Thin-Film Titanium–Platinum Microelectrodes and Their Comparison to Classic, Wire-Based Platinum Microelectrodes in Selected Inorganic Electrolytes
This paper discusses the electrochemical properties of thin-film, planar, titanium–platinum (Ti-Pt) microelectrodes fabricated using glass or silicon substrates and compares their performance to the classic platinum (Pt) microelectrodes embedded in glass. To analyze the possible differences coming both from the size of the tested electrodes as well as from the substrate, short- and long-term electrochemical tests were performed on selected water electrolytes (KCl, HCl, KOH). To study the electrochemical response of the electrodes, the cyclic voltammetry (CV) measurements were carried out at different scanning rates (from 5 to 200 mV/s). Long-term tests were also conducted, including one thousand cycles with a 100 mV/s scan rate to investigate the stability of the tested electrodes. Before and after electrochemical measurements, the film morphology was analyzed using a scanning electron microscope (SEM). The good quality of the thin-film Pt electrodes and the high repeatability in electrochemical response have been shown. There are minor differences in standard deviation values taken from electrochemical measurements, comparing thin-film and wire-based electrodes. Damages or any changes on the electrodes’ surfaces were revealed by SEM observations after long-term electrochemical tests.